Electrophysical Properties of Microalloyed Alumo-Silicate Ceramics as Active Dielectric

Abstract

In this paper, electrophysical properties of porous alumo-silicate ceramics, modified by alloying with magnesium and microalloying with aluminum, were investigated. Complex multiphase system, as active microalloyed ceramics, has specific behavior under influence of external electrical field, which involves changes of dielectric losses and impedance, depending on frequency and temperature. Dielectric properties were measured in the frequency range 20 Hz – 1 MHz. Values for permittivity (εr) ranged between 140 – 430. Order of magnitude for electrical resistivity was about 106 Ωm, for impedance 104 – 108 Ω, and loss tangent had values about and greater than 0.05. Current flow through active dielectric takes place through dielectric barrier and throughout conduction bands of thin aluminum and magnesium metal films. Permittivity has nonlinear distribution and complex functional dependences because of significant nonhomogeneity of active microalloyed ceramics. Lower values of electrical resistivity are the result of complex electron and ion transfer of charge through solid phase and pores, with decreased potential barriers height, due to the influence of additives, ingredients and defects.